5.1 Surface grinding can cause a significant decrease4 in the flexure strength of advanced ceramic materials. The magnitude of the loss in strength is determined by the grinding conditions and the response of the material. This test method can be used to obtain a detailed characterization of the relationship between grinding conditions and flexure strength for an advanced ceramic material. The effect on flexure strength of varying a single grinding parameter or several grinding parameters can be measured. The method may also be used to compare and rank different materials according to their response to one or more different grinding conditions. Results obtained by this method can be used to develop an optimum grinding process with respect to maximizing material removal rate for a specified flexure strength requirement. The test method can assist in the development of improved grinding-damage-tolerant ceramic materials. It may also be used for quality control purposes to monitor and assure the consistency of a grinding process in the fabrication of parts from advanced ceramic materials. The test method is applicable to grinding methods that generate a planar surface and is not directly applicable to grinding methods that produce non-planar surfaces such as cylindrical and centerless grinding.1.1 This test method covers the determination of the effect of surface grinding on the flexure strength of advanced ceramics. Surface grinding of an advanced ceramic material can introduce microcracks and other changes in the near surface layer, generally referred to as damage (see Fig. 1 and Ref. (1)).2 Such damage can result in a change—most often a decrease—in flexure strength of the material. The degree of change in flexure strength is determined by both the grinding process and the response characteristics of the specific ceramic material. This method compares the flexure strength of an advanced ceramic material after application of a user-specified surface grinding process with the baseline flexure strength of the same material. The baseline flexure strength is obtained after application of a surface grinding process specified in this standard. The baseline flexure strength is expected to approximate closely the inherent strength of the material. The flexure strength is measured by means of ASTM flexure test methods.FIG. 1 Microcracks Associated with Grinding (Ref. (1))21.2 Flexure test methods used to determine the effect of surface grinding are C1161 Test Method for Flexure Strength of Advanced Ceramics at Ambient Temperatures and C1211 Test Method for Flexure Strength of Advanced Ceramics at Elevated Temperatures.1.3 Materials covered in this standard are those advanced ceramics that meet criteria specified in flexure testing standards C1161 and C1211.1.4 The flexure test methods supporting this standard (C1161 and C1211) require test specimens that have a rectangular cross section, flat surfaces, and that are fabricated with specific dimensions and tolerances. Only grinding processes that are capable of generating the specified flat surfaces, that is, planar grinding modes, are suitable for evaluation by this method. Among the applicable machine types are horizontal and vertical spindle reciprocating surface grinders, horizontal and vertical spindle rotary surface grinders, double disk grinders, and tool-and-cutter grinders. Incremental cross-feed, plunge, and creep-feed grinding methods may be used.1.5 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

定价： 646元 / 折扣价： 550 元 加购物车

4.1 The grinding materials used for the preparation of the surfaces of specimens prior to analysis by spark atomic emission or X-ray fluorescence spectrometry can contaminate the surface and thus produce erroneous results. This guide provides examples of the effects of these contaminations and recommendations for evaluating grinding materials to eliminate or reduce these effects in spectrochemical analysis.4.2 The examples given in this guide are not the only contaminations that can occur. Especially in X-ray spectrometry, all phases of the surface preparation should be examined for potential contamination effects.4.3 Analytical significance of the contaminations observed depends on the needs of the analyst for the particular application at a given composition.1.1 This guide covers recommendations for the evaluation of various grinding materials used to prepare the surfaces of specimens to be analyzed by spark atomic emission or X-ray fluorescence spectrometry.1.2 This standard does not purport to address all of the safety problems, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

定价： 590元 / 折扣价： 502 元 加购物车

定价： 525元 / 折扣价： 468 元 加购物车