This specification covers sheet steel in coils and cut lengths coated with lead-tin alloy by the hot-dip process. The material, also known as terne-coated sheet, is available in four designations as commercial steel, deep drawing steel, extra deep drawing steel, and structural steel. Amount of copper, nickel, chromium, molybdenum, vanadium, titanium, columbium, and boron shall conform to the chemical composition requirements of this specification. Yield strength, tensile strength, elongation, and bending shall conform to the mechanical property requirements.1.1 This specification covers sheet steel in coils and cut lengths coated with lead-tin alloy (terne metal, see 3.2.3) by the hot-dip process. This material is commonly known as terne and is used where ease of solderability and a degree of corrosion resistance are desirable. It is especially suitable where resistance to gasoline is required. Terne-coated sheet is also used for stamping, where the coating acts as a lubricant in the die, lessening difficulties in drawing. The weight of coating, always expressed as total coating on both sides, shall be specified in accordance with Table 1.1.2 Material furnished under this specification shall conform to the applicable requirements of the latest issue of Specification A924/A924M, unless otherwise provided herein.1.3 Terne-coated steel is available in a number of designations, types, and grades.1.4 This specification is applicable to orders in either inch-pound units (as A308) or SI units (as A308M). Values in inch-pound and SI units are not necessarily equivalent. Within the text, SI units are shown in brackets. Each system shall be used independently of the other.1.5 Unless the order specifies the “M” designation (SI units), the product shall be furnished to inch-pound units.1.6 The text of this specification references notes and footnotes that provide explanatory material. These notes and footnotes, excluding those in tables and figures, shall not be considered as requirements of this specification.1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

定价： 0元 / 折扣价： 0 元

3.1 A coating of terne metal on iron or steel articles is intended to provide drawability, solderability, or corrosion resistance, or combination thereof, which can require different amounts of coating. Specifications for terne-coated sheets frequently provide for these different classes (weights) of coating so that purchasers can select that most suitable for their needs. This test method provides a means of determining the weight of coating for comparison with the material specification requirements. 1.1 This test method covers the determination of the weight and composition of coating on terne sheet by the triple-spot method. The following three procedures are described: 1.1.1 Procedure A—Stripping with sulfuric acid. 1.1.2 Procedure D—Stripping with hydrochloric acid and antimony trichloride. 1.1.3 Procedure E—Stripping with hydrobromic acid-bromine solution. Note 1—Procedure B (Electrolytic Stripping) and Procedure C (Stripping with Silver Nitrate Solution), formerly in this test method, were discontinued because lack of usage. The designation for Procedure D and Procedure E are retained to avoid future confusion when reference is made only to the procedure designation. 1.2 If the percent of tin in the coating is required, stripping with hydrobromic acid-bromine is the preferred procedure. Steel with a predeposited electrolytic nickel coating requires a two-stage stripping method to determine total tin content. If both the tin and lead percentage are required, stripping with sulfuric acid is recommended, but caution is advised since the sulfuric acid procedure has been found to produce high tin results (see Section 11). 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. For specific hazards statements, see Section 5, Note 2, and Section 17.

定价： 0元 / 折扣价： 0 元