【国外标准】 Standard Test Method for Apparent Viscosity of Hydrocarbon Resins at Elevated Temperatures
本网站 发布时间:
2024-02-28
开通会员免费在线看70000余条国内标准,赠送文本下载次数,单本最低仅合13.3元!还可享标准出版进度查询、定制跟踪推送、标准查新等超多特权!  
查看详情>>

适用范围:
5.1 This test method is used to measure the apparent viscosity of hydrocarbon resins at elevated temperatures. Elevated temperature viscosity values of a hydrocarbon resin may be related to the properties of coatings, adhesives and the like, containing such a resin.5.2 For hydrocarbon resins, values of apparent viscosity will usually be a function of shear rate under the conditions of test. Although the type of viscometer described in this test method operates under conditions of relatively low shear rate, shear rate depends on the spindle and rotational speed selected for a determination; therefore, comparisons between apparent viscosity values should be made only for measurements made with similar viscometers under conditions of equivalent shear rate.1.1 This test method covers the determination of the apparent viscosity of hydrocarbon resins having apparent viscosities up to 2,000,000 millipascal seconds (mPa·s) (Note 1) at temperatures up to 300 °C [572 °F].NOTE 1: The SI unit of (dynamic) viscosity is the pascal second. The centipoise (cP) is one millipascal second (mPa·s) and is frequently used as a viscosity unit.1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
标准号:
ASTM D6267/D6267M-13(2022)
标准名称:
Standard Test Method for Apparent Viscosity of Hydrocarbon Resins at Elevated Temperatures
英文名称:
Standard Test Method for Apparent Viscosity of Hydrocarbon Resins at Elevated Temperatures标准状态:
Active-
发布日期:
-
实施日期:
出版语种:
- 其它标准
- 上一篇: ASTM D6266-00a(2023) Standard Test Method for Determining the Amount of Volatile Organic Compound (VOC) Released From Waterborne Automotive Coatings and Available for Removal in a VOC Control Device (Abatement)
- 下一篇: ASTM D6268-21 Standard Practice for Handling, Transportation, and Storage of HFC-125, Pentafluoroethane (C2HF5)
- 推荐标准
- ASTM C117-23 Standard Test Method for Materials Finer than 75-μm (No. 200) Sieve in Mineral Aggregates by Washing
- ASTM C1170/C1170M-20 Standard Test Method for Determining Consistency and Density of Roller-Compacted Concrete Using a Vibrating Table
- ASTM C1173-22 Standard Specification for Flexible Transition Couplings for Underground Piping Systems
- ASTM C1174-20 Standard Guide for Evaluation of Long-Term Behavior of Materials Used in Engineered Barrier Systems (EBS) for Geological Disposal of High-Level Radioactive Waste
- ASTM C1177/C1177M-17 Standard Specification for Glass Mat Gypsum Substrate for Use as Sheathing
- ASTM C1178/C1178M-18 Standard Specification for Coated Glass Mat Water-Resistant Gypsum Backing Panel
- ASTM C1181/C1181M-17 Standard Test Methods for Compressive Creep of Chemical-Resistant Polymer Machinery Grouts
- ASTM C1184-23 Standard Specification for Structural Silicone Sealants
- ASTM C1185-23 Standard Test Methods for Sampling and Testing Fiber-Cement Flat Sheet, Roofing and Siding Shingles, and Clapboards
- ASTM C1186-22e1 Standard Specification for Flat Fiber-Cement Sheets
- ASTM C1190-18(2022) Standard Practice for Location of Test Specimens from Magnesia-Carbon and Impregnated Burned Basic Brick
- ASTM C1193-16(2023) Standard Guide for Use of Joint Sealants
- ASTM C1195-21 Standard Test Method for Absorption of Architectural Cast Stone
- ASTM C1196-20 Standard Test Method for In Situ Compressive Stress Within Solid Unit Masonry Estimated Using Flatjack Measurements
- ASTM C12-22a Standard Practice for Installing Vitrified Clay Pipe Lines