3.1 This practice can be used to extract carbides, borides, TCP and GCP phases, which can then be qualitatively or quantitatively analyzed by X-ray diffraction or microanalysis.23.2 Careful control of parameters is necessary for reproducible quantitative results. Within a given laboratory, such results can be obtained routinely; however, caution must be exercised when comparing quantitative results from different laboratories.33.3 Comparable qualitative results can be obtained routinely among different laboratories using this procedure.31.1 This practice covers a procedure for the isolation of carbides, borides, TCP (topologically close-packed), and GCP (geometrically close-packed) phases (Note 1) in nickel and nickel-iron base gamma prime strengthened alloys. Contamination of the extracted residue by coarse matrix (gamma) or gamma prime particles, or both, reflects the condition of the alloy rather than the techniques mentioned in this procedure.1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. (See 4.3.2.1 and 5.1.1.)NOTE 1: Ni3 Ti (eta phase) has been found to be soluble in the electrolyte for some alloys.FIG. 1 Schematic Diagram of Extraction Cell1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

定价： 0元 / 折扣价： 0 元

This specification covers electric fusion-welded nickel-chromium-cobalt-molybdenum alloy UNS N06617, nickel-iron-chromium-silicon alloys UNS N08330 and UNS N08332, Ni-Cr-Fe-Al Alloy (UNS N06603), Ni-Cr-Fe Alloy UNS N06025, and Ni-Cr-Fe-Si Alloy UNS N06045 pipe intended for heat resisting applications and general corrosive service. Two classes of pipes are covered: Class 1 and Class 2. The joints shall be double-welded, full-penetration welds. The weld shall be made either manually or automatically by an electric process involving the deposition of filler metal. Weld defects shall be repaired by removal to sound metal and rewelding. All pipe shall be furnished in the annealed condition. The material shall conform to the composition limits specified. Transverse tension test, transverse guided-bend weld test, pressure test, and chemical analysis shall be made to conform to the requirements specified.1.1 This specification covers electric fusion-welded nickel-chromium-cobalt-molybdenum alloy UNS N06617, nickel-iron-chromium-silicon alloys UNS N08330 and UNS N08332, Ni-Cr-Fe-Al Alloy (UNS N06603), Ni-Cr-Fe Alloy UNS N06025, and Ni-Cr-Fe-Si Alloy UNS N06045 pipe intended for heat resisting applications and general corrosive service.1.2 This specification covers pipe in sizes 3 in. (76.2 mm) nominal diameter and larger and possessing a minimum wall thickness of 0.083 in. (2.11 mm).1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

定价： 515元 / 折扣价： 438 元 加购物车

定价： 无文本 / 折扣价： 0 元

本标准规定了Ni-Cr-B-Si系自熔合金粉的要求、试验方法、检验规则及标志、包装、运输、贮存、质量证明书和合同（或订货单）内容。
本标准适用于氧-乙炔喷焊、感应重熔、等离子堆焊和激光熔覆用Ni-Cr-B-Si系自熔合金粉。

定价： 21元 / 折扣价： 18 元 加购物车

定价： 19元 / 折扣价： 17 元 加购物车