【国外标准】 Standard Test Methods for Determination of Gel Content and Swell Ratio of Crosslinked Ethylene Plastics
本网站 发布时间:
2024-02-28
开通会员免费在线看70000余条国内标准,赠送文本下载次数,单本最低仅合13.3元!还可享标准出版进度查询、定制跟踪推送、标准查新等超多特权!  
查看详情>>

适用范围:
5.1 Many important properties of crosslinked ethylene plastics vary with the gel content. Hence, determination of the gel content provides a means of both controlling the process and rating the quality of finished products.5.2 Extraction tests permit verification of the proper gel content of any given crosslinked ethylene plastic and they also permit comparison between different crosslinked ethylene plastics, including those containing fillers, provided that, for the latter, the following conditions are met:5.2.1 The filler is not soluble in either decahydronaphthalene or xylenes at the extraction temperature.5.2.2 The amount of filler present in the compound either is known or will be determined by other means.5.2.3 Sufficient crosslinking has been achieved to prevent migration of filler during the extraction. Usually it has been found that, at extraction levels up to 50 %, the extractant remains clear and free of filler.5.3 A suitable antioxidant is added to the extractant to inhibit possible oxidative degradation at the extraction temperatures.5.4 Before proceeding with this test method, reference shall be made to the specification of the material being tested. Any test specimen preparation, conditioning, dimensions, or testing parameters, or a combination thereof, covered in the materials specification shall take precedence over those mentioned in this test method. If there are no material specifications, then the default conditions apply.1.1 The gel content (insoluble fraction) produced in ethylene plastics by crosslinking is determined by extracting with solvents such as decahydronaphthalene or xylenes. The methods described herein are applicable to crosslinked ethylene plastics of all densities, including those containing fillers, and all provide corrections for the inert fillers present in some of those compounds.1.2 Test Method A, which permits most complete extraction in least time, is to be used for referee tests, but two alternative nonreferee Test Methods B and C are also described. Test Method B differs from the referee test method only in sample preparation; that is, it requires use of shavings taken at selected points in cable insulation, for example, rather than the ground sample required by the referee test method. Because the shaved particles are larger, less total surface per sample is exposed to the extractant, so this test method ordinarily yields extraction values about 1 to 2 % lower than the referee method. Test Method C requires that a specimen in one piece be extracted in xylenes at a constant temperature of 110°C. At this temperature and with a one-piece specimen, even less extraction occurs (from 3 to 9 % less than the referee test method), this method permits swell ratio (a measure of the degree of crosslinking in the gel phase) be determined.1.3 Extraction tests are made on articles of any shape. They have been particularly useful for electrical insulations since specimens can be selected from those portions of the insulation most susceptible to insufficient crosslinking.1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.NOTE 1: This test method is equivalent to ISO 10147, Method B. It is not equivalent to ISO 10147 in any other measurement or section.1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. Specific precautionary statements are given in Sections 6, 9, and 24.
标准号:
ASTM D2765-16
标准名称:
Standard Test Methods for Determination of Gel Content and Swell Ratio of Crosslinked Ethylene Plastics
英文名称:
Standard Test Methods for Determination of Gel Content and Swell Ratio of Crosslinked Ethylene Plastics标准状态:
Historical-
发布日期:
-
实施日期:
出版语种:
- 推荐标准
- ASTM D4919-23 Standard Guide for Testing of Hazardous Materials (Dangerous Goods) Packagings
- ASTM D4921-20 Standard Test Method for Foaming Tendencies of Engine Coolants at Room Temperature
- ASTM D4926-20 Standard Test Method for Gamma Alumina Content in Catalysts and Catalyst Carriers Containing Silica and Alumina by X-ray Powder Diffraction
- ASTM D4927-20 Standard Test Methods for Elemental Analysis of Lubricant and Additive Components—Barium, Calcium, Phosphorus, Sulfur, and Zinc by Wavelength-Dispersive X-Ray Fluorescence Spectroscopy
- ASTM D4928-12(2018) Standard Test Method for Water in Crude Oils by Coulometric Karl Fischer Titration
- ASTM D4930-23 Standard Test Method for Dust Control Material on Calcined Petroleum Coke
- ASTM D4932/D4932M-89(2019) Standard Test Method for Fastener Rupture and Tear Resistance of Roofing and Waterproofing Sheets, Roll Roofing, and Shingles
- ASTM D4933-16(2021) Standard Guide for Moisture Conditioning of Wood and Wood-Based Materials
- ASTM D4934-02(2021) Standard Test Method for Rubber Compounding Materials: 2-Benzothiazyl Sulfenamide Accelerators—Insolubles
- ASTM D4935-18 Standard Test Method for Measuring the Electromagnetic Shielding Effectiveness of Planar Materials
- ASTM D4936-10(2023) Standard Test Method for Mercaptobenzothiazole Sulfenamide Assay by Reduction/Titration
- ASTM D4937-96(2021) Standard Test Method for p-Phenylenediamine Antidegradants Purity by Gas Chromatography
- ASTM D4939-89(2020) Standard Test Method for Subjecting Marine Antifouling Coating to Biofouling and Fluid Shear Forces in Natural Seawater
- ASTM D4940-15(2020) Standard Test Method for Conductimetric Analysis of Water Soluble Ionic Contamination of Blast Cleaning Abrasives
- ASTM D4941-06(2021) Standard Practice for Preparing Drawdowns of Artists’ Paste Paints