【国外标准】 Standard Test Method for Fracture Strength in Cleavage of Adhesives in Bonded Metal Joints
本网站 发布时间:
2024-02-28
开通会员免费在线看70000余条国内标准,赠送文本下载次数,单本最低仅合13.3元!还可享标准出版进度查询、定制跟踪推送、标准查新等超多特权!  
查看详情>>
标准简介
适用范围:
NOTE 2: Crack growth in adhesive bond specimens can proceed in two ways: (1) by a slow-stable extension where the crack velocity is dictated by the crosshead rate or (2) by a run-arrest extension where the stationary crack abruptly jumps ahead outrunning the crosshead-predicted rate. The first type of crack extension is denoted flat; the second type peaked because of the appearance of the autographic record. The flat behavior is characteristic of adhesives or test temperatures, or both, for these adhesives where there is no difference between initiation, G1c, and arrest, G1a. For example, the rubber modified film adhesives tested above −17.8°C (0°F) all exhibit flat autographic records. Peaked curves are exhibited for all modified materials tested below −73°C (−100°F) and in general for unmodified epoxies.It should be noted that both peaked and flat behaviors are determined from a crack-length-independent specimen. For other specimens or structures where G increases with a at constant load the onset of crack growth would result in rapid complete fracturing whatever the adhesive characteristics.5.1 The property G1c (and G1a if relevant) determined by this test method characterizes the resistance of a material to slow-stable or run-arrest fracturing in a neutral environment in the presence of a sharp crack under severe tensile constraint, such that the state of stress near the crack front approaches tritensile plane strain, and the crack-tip plastic region is small compared with the crack size and specimen dimensions in the constraint direction. It has not been proven that tough adhesive systems fully meet this criteria. Therefore, data developed using equations based on this assumption may not represent plane-strain fracture values. Comparison of fracture toughness between adhesive systems widely different in brittleness or toughness should take this into consideration. In general, systems of similar type toughness (6, 7, 8, 9, 10) can be compared as can the effect of environment on toughness of a single system. A G1c value is believed to represent a lower limiting value of fracture toughness for a given temperature, strain rate, and adhesive condition as defined by manufacturing variables. This value may be used to estimate the relation between failure stress and defect size for a material in service wherein the conditions of high constraint described above would be expected. Background information concerning the basis for development of this test method in terms of linear elastic fracture mechanics may be found in Refs (4) and (8).5.1.1 Cyclic loads can cause crack extension at G1 values less than G1c value. Furthermore, progressive stable crack extension under cyclic or sustained load may be promoted by the presence of certain environments. Therefore, application of G1c in the design of service components should be made with awareness of the G increase for a prior crack which may occur in service due to slow-stable crack-extension.5.2 This test method can serve the following purposes:5.2.1 In research and development to establish, in quantitative terms, significant to service performance, the effects of adhesive composition, primers, adherend surface treatments, supporting adhesive carriers (scrim), processing variables, and environmental effects.5.2.2 In service evaluation to establish the suitability of an adhesive system for a specific application for which the stress conditions are prescribed and for which maximum flaw sizes can be established with confidence.5.2.3 For specifications of acceptance and manufacturing quality control, but only when there is a sound basis for specification of minimum G1c values. The specification of G1c values in relation to a particular application should signify that a fracture control study has been conducted on the component in relation to the expected history of loading and environment, and in relation to the sensitivity and reliability of the crack detection procedures that are to be applied prior to service and subsequently during the anticipated life.1.1 This test method (1, 2, 3, 4, 5)2 covers the determination of fracture strength in cleavage of adhesives when tested on standard specimens and under specified conditions of preparation and testing (Note 1).1.2 This test method is useful in that it can be used to develop design parameters for bonded assemblies.NOTE 1: While this test method is intended for use in metal-to-metal applications it may be used for measuring fracture properties of adhesives using plastic adherends, provided consideration is given to the thickness and rigidity of the plastic adherends.1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
标准号:
ASTM D3433-99(2020)
标准名称:
Standard Test Method for Fracture Strength in Cleavage of Adhesives in Bonded Metal Joints
英文名称:
Standard Test Method for Fracture Strength in Cleavage of Adhesives in Bonded Metal Joints标准状态:
Active-
发布日期:
-
实施日期:
出版语种:
- 其它标准
- 上一篇: ASTM D3432-89(1996)e1 Standard Test Method for Unreacted Toluene Diisocyanates in Urethane Prepolymers and Coating Solutions by Gas Chromatography (Withdrawn 2004)
- 下一篇: ASTM D3434-00(2018) Standard Test Method for Multiple-Cycle Accelerated Aging Test (Automatic Boil Test) for Exterior Wet Use Wood Adhesives
- 推荐标准
- 国家标准计划
- BS ISO 24138:2024 Information and documentation. International Standard Content Code (ISCC)
- 24/30492859 DC BS EN IEC 61753-1 Fibre optic interconnecting devices and passive components - Performance standard
- BS EN IEC 61753-071-02:2020+A1:2024 Fibre optic interconnecting devices and passive components. Performance standard
- 24/30491443 DC standard
- 24/30489392 DC BS EN IEC 62358 Ferrite cores. Standard inductance factor for gapped cores and its tolerance
- BS ISO 19848:2024 - TC Tracked Changes. Ships and marine technology. Standard data for shipboard machinery and equipment
- BS ISO 19848:2024 Ships and marine technology. Standard data for shipboard machinery and equipment
- BS IEC 61360-7:2024 Standard data element types with associated classification scheme
- 24/30487130 DC BS EN 50566:2017/A2:2024 Product standard to demonstrate the compliance of wireless communication
- 24/30486472 DC - Product standard
- KS M ISO 4259-4 석유 및 관련 제품 — 측정 방법과 결과의 정밀도 — 제4부: 개별 실험실에서 표준 시험방법의 실행에 대한 ‘통계적 관리’ 상태를 확인하기 위한 통계적 관리도의 사용
- KS C IEC 61340-4-6 정전기학 — 제4-6부: 구체적 적용 분야에 대한 표준 시험방법 — 손목접지대
- KS C IEC 61340-4-7 정전기학 — 제4-7부: 구체적 적용 분야에 대한 표준 시험방법 — 이온화
- KS C IEC 61340-4-8 정전기학 — 제4-8부: 구체적 적용 분야에 대한 표준 시험방법 — ESD 차폐성 — 봉투
- 24/30485973 DC standard