【国外标准】 Standard Specification for High-Strength Low-Alloy Welded and Seamless Steel Pipe (Withdrawn 2014)
本网站 发布时间:
2024-02-28
- ASTM A714-99(2009)e1
- Withdrawn, No replacement
- 定价: 0元
- 在线阅读
开通会员免费在线看70000余条国内标准,赠送文本下载次数,单本最低仅合13.3元!还可享标准出版进度查询、定制跟踪推送、标准查新等超多特权!  
查看详情>>

适用范围:
This specification covers standard requirements for seamless and welded high-strength low-alloy steel pipe NPS ½ to NPS 26, inclusive. The material shall be utilized in pressure piping service, and other general purposes, where savings in weight or added durability are important. Heat and product analysis shall be performed wherein different grades of steel shall conform to the required chemical composition for carbon, manganese, phosphorus, sulfur, silicon, copper, vanadium, nickel, chromium, and molybdenum. The material shall conform to the required tensile properties such as tensile strength, yield strength, and elongation for the grade of Class 2 or Class 4 pipe specified. The steel shall undergo the following mechanical tests, namely: bend test, flattening test, and hydrostatic test.1.1 This specification covers seamless and welded high-strength low-alloy steel pipe NPS 1/2 to NPS 26, inclusive. Pipe having other dimensions may be furnished provided such pipe complies with all other requirements of this specification. This material is intended for pressure piping service, and other general purposes, where savings in weight or added durability are important. Note 1—The dimensionless designator NPS (nominal pipe size) has been substituted in this standard for such traditional terms as “nominal diameter,” “size,” and “nominal size.” Note 2—A comprehensive listing of standardized pipe dimensions is contained in ANSI Standard B36.10. 1.2 Class—These high-strength low-alloy steels have enhanced resistance to general atmospheric corrosion by weathering as commonly encountered in rural, urban, marine, and industrial environments. They are supplied in two classes: Class 2, having corrosion resistance equivalent to that of carbon steel with copper (0.20 minimum Cu); and Class 4, having corrosion resistance substantially better than that of Class 2 (Note 3). Class 4 steels when properly exposed to the atmosphere can be used bare (unpainted) for many applications. Note 3—For methods of estimating the atmospheric corrosion resistance of low alloy steels see Guide G 101 or actual data. 1.3 Type—Pipe may be furnished in the following types of manufacturing processes:Type F—Furnace-butt welded, continuous welded,Type E—Electric-resistance welded, andType S—Seamless. 1.3.1 Pipe ordered under this specification is suitable for welding. 1.3.2 Type E pipe may be furnished either nonexpanded or cold-expanded at the option of the manufacturer. 1.3.3 Types F, E, and S pipe are commonly furnished in nonheat-treated condition. Type S pipe may be furnished in normalized (or other) heat-treated condition, when so specified. 1.3.4 Types F, E, and S pipe in single random lengths may be furnished with hot-dipped galvanized coating of zinc, subject to inquiry to the producer. 1.3.5 Couplings, when furnished, shall be of the same class, heat-treated condition, and grade of material as the pipe ordered. 1.4 Grade—This specification designates eight grades of steel composition as listed in Table 1 and corresponding tensile requirements for the grades as listed in Table 2. 1.4.1 For Class 2 pipe, Grade I, II, or III shall be specified, and copper-bearing steel is required as specified in Table 1. 1.4.2 For Class 4 pipe, Grade IV, V, VI, VII, or VIII shall be specified. Alternatively, for Class 4, Type S, and Type E pipe, a steel composition corresponding to a grade listed in Table 1 of Specification A 588/A 588M may be specified, subject to negotiation. 1.5 When Class 4 pipe is joined by welding or is used in welded construction, the user is cautioned that the selection of welding procedure and resultant composition of fused metal should be suitable for Class 4 material and the intended service. 1.6 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
标准号:
ASTM A714-99(2009)e1
标准名称:
Standard Specification for High-Strength Low-Alloy Welded and Seamless Steel Pipe (Withdrawn 2014)
英文名称:
Standard Specification for High-Strength Low-Alloy Welded and Seamless Steel Pipe (Withdrawn 2014)标准状态:
Withdrawn, No replacement-
发布日期:
-
实施日期:
出版语种:
- 其它标准
- 上一篇: ASTM A713-04(2017) Standard Specification for Steel Wire, High-Carbon Spring, for Heat-Treated Components
- 下一篇: ASTM A715-98 Standard Specification for Steel Sheet and Strip, High-Strength, Low-Alloy, Hot-Rolled, and Steel Sheet, Cold-Rolled, High-Strength, Low-Alloy, with Improved Formability (Withdrawn 2000)
- 推荐标准
- ASTM E316-17 Standard Test Method for Determination of Iron in Manganese Ores by Hydrogen Sulfide Reduction-Dichromate Titrimetry
- ASTM E3161-21 Standard Practice for Preparing a Pseudomonas aeruginosa or Staphylococcus aureus Biofilm using the CDC Biofilm Reactor
- ASTM E3163-18 Standard Guide for Selection and Application of Analytical Methods and Procedures Used during Sediment Corrective Action
- ASTM E3164-23 Standard Guide for Contaminated Sediment Site Risk-Based Corrective Action – Baseline, Remedy Implementation and Post-Remedy Monitoring Programs
- ASTM E3166-20e1 Standard Guide for Nondestructive Examination of Metal Additively Manufactured Aerospace Parts After Build
- ASTM E3168-20a Standard Practice for Determining Low-Contrast Visual Acuity of Radiographic Interpreters
- ASTM E317-21 Standard Practice for Evaluating Performance Characteristics of Ultrasonic Pulse-Echo Testing Instruments and Systems without the Use of Electronic Measurement Instruments
- ASTM E3170/E3170M-18(2023) Standard Practice for Phased Array Ultrasonic Testing of Polyethylene Electrofusion Joints
- ASTM E3171-21a Standard Test Method for Determination of Total Silver in Textiles by ICP-OES or ICP-MS Analysis
- ASTM E3178-18 Standard Practice for Evaluating Static and Cidal Chemical Decontaminants against Bacillus Spores using Centrifugal Filtration Tubes
- ASTM E3182-20 Standard Practice for Preparing an Occupant Exposure Screening Report (OESR) for Substances in Installed Building Products
- ASTM E3186-19 Standard Guide for Use and Testing of Dry-Block Temperature Calibrators
- ASTM E3191-18 Standard Specification for Permanent Foaming Fixatives Used to Mitigate Spread of Radioactive Contamination
- ASTM E3192/E3192M-20 Standard Practice for Soft Armor Conditioning by Tumbling
- ASTM E3197-23 Standard Terminology Relating to Examination of Fire Debris