This specification covers aluminum and aluminum-alloy die forgings, hand forgings, and rolled ring forgings and includes the following UNS alloy designations: A91100, A92014, A92018, A92025, A92219, A92618, A93003, A94032, A95083, A96061, A96066, A96151, A97049, A97050, A97075, A97076, and A97175. Tempers covered by this specification includes: H112, T4, T6, T61, T73, T74, T7352, T7452, T7454, T652, T852, and H111 as well as F and 01 types. The forgings may be manufactured by pressing, hammering, or rolling, at the option of the producer. Requirements for quality assurance, chemical analysis, tension and hardness tests, heat treatment, heat-treat response, and stress corrosion resistance and stress-corrosion cracking test are detailed. The forgings shall conform to the chemical composition requirements prescribed for aluminum, silicon, iron, copper, manganese, magnesium, chromium, nickel, zinc, zirconium, and titanium. Forgings having the specified thickness shall meet the requirements specified for the mechanical properties such as tensile strength, yield strength, elongation, and Brinell hardness. 1.1 This specification2 covers aluminum-alloy (Note 1) die forgings, hand forgings, and rolled ring forgings as shown in Table 2, Table 3, and Table 4 in Section 10 for heat-treatable alloy forgings supplied in the F and 01 tempers. The maximum thicknesses for forgings within the scope of this specification are as indicated in those tables. Note 1: Throughout this specification use of the term alloy in the general sense includes aluminum as well as aluminum alloy. Note 2: For forging stock supplied as rolled, cold-finished bar, extruded bar, or rod see Specification B211/B211M. 1.2 Alloy and temper designations are in accordance with ANSI H35.1/H35.1(M). The equivalent Unified Numbering System alloy designations are those of Table 1 preceded by A9, for example, A91100 for aluminum 1100 in accordance with Practice E527. 1.3 For acceptance criteria for inclusion of new aluminum and aluminum alloys in this specification, see Annex A2. 1.4 This specification is the inch-pound companion to Specification B247M; therefore, no SI equivalents are presented in the specification. 1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

定价： 646元 / 折扣价： 550 元 加购物车

This specification covers aluminum and aluminum-alloy die forgings, hand forgings, and rolled ring forgings and includes the following UNS alloy designations: A91100, A92014, A92018, A92025, A92219, A92618, A93003, A94032, A95083, A96061, A96066, A96151, A97049, A97050, A97075, A97076, and A97175. Tempers covered by this specification includes: H112, T4, T6, T61, T73, T74, T7352, T7452, T7454, T652, T852, and H111 as well as F and 01 types. The forgings may be manufactured by pressing, hammering, or rolling, at the option of the producer. Requirements for quality assurance, chemical analysis, tension and hardness tests, heat treatment, heat-treat response, and stress corrosion resistance and stress-corrosion cracking test are detailed. The forgings shall conform to the chemical composition requirements prescribed for aluminum, silicon, iron, copper, manganese, magnesium, chromium, nickel, zinc, zirconium, and titanium. Forgings having the specified thickness shall meet the requirements specified for the mechanical properties such as tensile strength, yield strength, elongation, and Brinell hardness. 1.1 This specification covers aluminum-alloy (Note 1) die forgings, hand forgings, and rolled ring forgings as shown in Tables 2-4 and in Section 10 for heat-treatable alloy forgings supplied in the F and 01 tempers. The maximum thicknesses for forgings within the scope of this specification are as indicated in those tables. Note 1: Throughout this specification use of the term alloy in the general sense includes aluminum as well as aluminum alloy. Note 2: For forging stock supplied as rolled or cold-finished bar or rod see Specification B211/B211M. For forging stock supplied as extruded bar or rod see Specification B221M. 1.2 Alloy and temper designations are in accordance with ANSI H35.1/H35.1(M). The equivalent Unified Numbering System alloy designations are those of Table 1 preceded by A9, for example, A91100 for aluminum 1100 in accordance with Practice E527. 1.3 For acceptance criteria for inclusion of new aluminum and aluminum alloys in this specification, see Annex A2. 1.4 This specification is the SI companion to Specification B247. 1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

定价： 646元 / 折扣价： 550 元 加购物车

This specification establishes the general requirements common to several wrought products including copper and copper-alloy plates, sheets, strips, and rolled bars. The numerical values in this specification are not presented in inch-pound units, but rather, in metric or SI units only. The material for manufacture shall be a cast bar, cake, or slab of such purity and soundness as to be suitable for processing by hot- or cold-working, and annealing to produce a uniform wrought structure in the finished product. The edges shall be slit, sheared, sawed, or rolled, as specified. When rolled edges are required, they may be produced by either rolling or drawing to one of the following specified edge contours: square edges (square corners), rounded corners, rounded edges, and full-rounded edges. Products shall be sampled and prepared, then tested accordingly to examine their conformance to dimensional (thickness, length, width, weight, and straightness), mechanical (tensile and yield strength, Rockwell hardness, and elongation), electrical (resistivity and conductivity), chemical composition, and grain size requirements.1.1 This specification establishes the general requirements common to several wrought product specifications. Unless otherwise specified in the purchase order or in an individual specification, these general requirements shall apply to copper and copper-alloy plate, sheet, strip, and rolled bar supplied under each of the following product specifications issued by ASTM: B19, B36/B36M, B96/B96M, B101, B103/B103M, B121/B121M, B122/B122M, B130, B152/B152M, B169/B169M, B194, B370, B422/B422M, B465, B534, B591, B592, B694, B740, B747, B768, B888/B888M, and B936.21.2 Units—This specification is the companion specification to SI Specification B248M; therefore, no SI equivalents are shown in this specification.1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

定价： 646元 / 折扣价： 550 元 加购物车