【国外标准】 Standard Test Method for Process Control Verification to Prevent Hydrogen Embrittlement in Plated or Coated Fasteners
本网站 发布时间:
2024-02-28
开通会员免费在线看70000余条国内标准,赠送文本下载次数,单本最低仅合13.3元!还可享标准出版进度查询、定制跟踪推送、标准查新等超多特权!  
查看详情>>
标准简介
适用范围:
5.1 This test method establishes a means to verify the prevention, to the extent possible, of IHE in steel fasteners during manufacture by maintaining strict controls during production operations such as surface preparation, pretreatments, and plating or coating. It is intended to be used as a qualification test for new or revised plating or coating processes and as a periodic inspection audit for the control of a plating or coating process.5.2 Passing this test allows fasteners to be stressed in tension to the minimum specified tensile load in air with almost no possibility of time delayed fracture in air as a result of IHE from processing. If the amount of residual hydrogen is not sufficient to induce cracking or fracture in the specimen under worst case conditions, then it can be concluded that all of the lots of fasteners processed during that period will not have sufficient residual hydrogen from processing to induce hydrogen embrittlement of the fasteners under stress in air if the process remains in control, unchanged and stable.5.3 If certified specimens with demonstrated sensitivity to IHE, processed with the fasteners, have a threshold ≥75 % of the incremental step load notched bend fracture stress, NFS(B)F1624, it is assumed that all fasteners processed the same way during the period will also pass any sustained load IHE test.FIG. 1 Dimensional Requirements for a 0.4W-Notched Square Bar Bend Specimen1.1 This test method covers a procedure to prevent, to the extent possible, internal hydrogen embrittlement (IHE) of fasteners by monitoring the plating or coating process, such as those described in Specifications F1137 and F1941. The process is quantitatively monitored on a periodic basis with a minimum number of specimens as compared to qualifying each lot of fasteners being plated or coated. Trend analysis is used to ensure quality as compared to statistical sampling analysis of each lot of fasteners. This test method consists of a mechanical test for the evaluation and control of the potential for IHE that may arise from various sources of hydrogen in a plating or coating process.1.2 This test method consists of a mechanical test, conducted on a standard specimen used as a witness, for the evaluation and control of the potential for IHE that may arise from various sources of hydrogen in a plating or coating process.1.3 This test method is limited to evaluating hydrogen induced embrittlement due only to processing (IHE) and not due to environmental exposure (EHE, see Test Method F1624).1.4 This test method is not intended to measure the relative susceptibility of steels to either IHE or EHE.1.5 This test method is limited to evaluating processes used for plating or coating ferrous fasteners.1.6 This test method uses a notched square bar specimen that conforms to Test Method F519, Type 1e, except that the radius is increased to accommodate the deposition of a larger range of platings and coatings. For the background on Test Method F519 testing, see publications ASTM STP 5432 and ASTM STP 962.3 The stress concentration factor is at a Kt = 3.1 ± 0.2. The sensitivity is demonstrated with a constant imposed cathodic potential to control the amount of hydrogen. Both the sensitivity and the baseline for residual hydrogen will be established with tests on bare metal specimens in air.1.7 The sensitivity of each lot of specimens to IHE shall be demonstrated. A specimen made of AISI E4340 steel heat treated to a hardness range of 50 to 52 HRC is used to produce a “worst case” condition and maximize sensitivity to IHE.1.8 The test is an accelerated (≤24 h) test method to measure the threshold for hydrogen stress cracking, and is used to quantify the amount of residual hydrogen in the specimen. The specimen undergoes sustained load and slow strain rate testing by using incremental loads and hold times under displacement control to measure a threshold stress in an accelerated manner in accordance with Test Method F1624.1.9 In this test method, bending is used instead of tension because it produces the maximum local limit load tensile stress in a notched bar of up to 2.3 times the yield strength as measured in accordance with Test Method E8/E8M. A fastener that is unintentionally exposed to bending on installation may attain this maximum local tensile stress.1.10 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.1.11 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.1.12 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
标准号:
ASTM F1940-07a(2019)
标准名称:
Standard Test Method for Process Control Verification to Prevent Hydrogen Embrittlement in Plated or Coated Fasteners
英文名称:
Standard Test Method for Process Control Verification to Prevent Hydrogen Embrittlement in Plated or Coated Fasteners标准状态:
Active-
发布日期:
-
实施日期:
出版语种:
- 推荐标准
- 国家标准计划
- BS EN IEC 61753-071-02:2020+A1:2024 Fibre optic interconnecting devices and passive components. Performance standard
- 24/30492859 DC BS EN IEC 61753-1 Fibre optic interconnecting devices and passive components - Performance standard
- 24/30491443 DC standard
- 24/30489392 DC BS EN IEC 62358 Ferrite cores. Standard inductance factor for gapped cores and its tolerance
- BS ISO 19848:2024 - TC Tracked Changes. Ships and marine technology. Standard data for shipboard machinery and equipment
- BS ISO 19848:2024 Ships and marine technology. Standard data for shipboard machinery and equipment
- 24/30487130 DC BS EN 50566:2017/A2:2024 Product standard to demonstrate the compliance of wireless communication
- BS IEC 61360-7:2024 Standard data element types with associated classification scheme
- 24/30486472 DC - Product standard
- KS M ISO 4259-4 석유 및 관련 제품 — 측정 방법과 결과의 정밀도 — 제4부: 개별 실험실에서 표준 시험방법의 실행에 대한 ‘통계적 관리’ 상태를 확인하기 위한 통계적 관리도의 사용
- KS C IEC 61340-4-7 정전기학 — 제4-7부: 구체적 적용 분야에 대한 표준 시험방법 — 이온화
- KS C IEC 61340-4-6 정전기학 — 제4-6부: 구체적 적용 분야에 대한 표준 시험방법 — 손목접지대
- KS C IEC 61340-4-8 정전기학 — 제4-8부: 구체적 적용 분야에 대한 표준 시험방법 — ESD 차폐성 — 봉투
- 24/30485973 DC standard
- BS EN 14662-1:2023 - TC Tracked Changes. Ambient air quality. Standard method for measurement of benzene concentrations