【国外标准】 Standard Practice for Lipid Preconditioning of Ultra-High-Molecular-Weight Polyethylene for Accelerated Aging
本网站 发布时间:
2024-02-28
开通会员免费在线看70000余条国内标准,赠送文本下载次数,单本最低仅合13.3元!还可享标准出版进度查询、定制跟踪推送、标准查新等超多特权!  
查看详情>>
标准简介
适用范围:
4.1 This practice summarizes two methods that may be used to precondition UHMWPE by the absorption of lipids to differentiate the simulated in vitro oxidative stability of UHMWPEs, after lipid exposure.4.1.1 Procedure A, High Squalene Absorption—This method of preconditioning with lipids may be used for comparative oxidative stability testing to screen different materials under aggressive conditions.4.1.2 Procedure B, Mixed Lipid Absorption—This method of preconditioning may be used for comparative oxidative stability testing under mild conditions that more closely simulate in-vivo conditions.4.2 This practice may be used to accelerate the oxidation of UHMWPE components when using elevated temperature and elevated oxygen pressure according to the methods of Practice F2003. Under real-time conditions such as implantation, oxidative changes to UHMWPE formulations may take months or years to produce changes that may result in deleterious mechanical performance. The method outlined in this practice permits the preparation of UHMWPE for evaluation of oxidative stability in a relatively short period of time (for example, weeks).4.3 This practice may also be used to precondition UHMWPE test specimens prior to characterization of their physical and chemical properties. In particular, this practice may be used for preconditioning with lipids prior to oxidation induction time (OIT) testing as outlined in Test Method D3895.1.1 It is the intent of this practice to permit an investigator to incorporate lipids found in the synovial environment into polymeric specimens. This can be used as a preconditioning step to evaluate the oxidative stability of ultra-high-molecular-weight polyethylene (UHMWPE) materials. This practice describes a laboratory procedure for preconditioning of UHMWPE specimens.1.2 The preconditioned UHMWPE can be aged at elevated temperature and at elevated oxygen pressure following methods of accelerated aging described in Practice F2003, to accelerate oxidation of the material and thereby allow for the evaluation of its long-term chemical stability.1.3 The preconditioned UHMWPE can be tested without further aging using a method to evaluate oxidative stability such as oxidation induction time as described in Test Method D3895.1.4 The methods of this practice may be used on any type of UHMWPE material intended for use in total joint arthroplasty in a synovial joint (for example, conventional, cross-linked, antioxidant stabilized, etc.). See Appendix X1.1.5 Although the preconditioning method followed by accelerated aging described by this practice will permit an investigator to compare the oxidative stability of different UHMWPE materials, it is recognized that this method is not known to simulate the degradative mechanisms for an implant during real-time shelf aging or in vivo. The described methods have not been evaluated for mechanical testing under cyclic loading.1.6 The preconditioning and accelerated aging methods specified herein are intended to rank the resistance to oxidation of materials as a result of the absorption of lipids, which may occur in UHMWPE following implantation, and to determine susceptibility to oxidative changes. The methods have not been evaluated for use in preconditioning of UHMWPE components for subsequent testing of mechanical or wear properties. Procedure A should not be used for preconditioning of UHMWPE components for subsequent testing of mechanical or wear properties.1.7 The values stated in SI units are to be regarded as standard. The values given in parentheses are mathematical conversions to inch-pound units that are for information only and are not considered standard.1.8 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.1.9 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
标准号:
ASTM F3336-22
标准名称:
Standard Practice for Lipid Preconditioning of Ultra-High-Molecular-Weight Polyethylene for Accelerated Aging
英文名称:
Standard Practice for Lipid Preconditioning of Ultra-High-Molecular-Weight Polyethylene for Accelerated Aging标准状态:
Active-
发布日期:
-
实施日期:
出版语种:
- 推荐标准
- 国家标准计划
- 24/30491443 DC standard
- 24/30489392 DC BS EN IEC 62358 Ferrite cores. Standard inductance factor for gapped cores and its tolerance
- BS ISO 19848:2024 - TC Tracked Changes. Ships and marine technology. Standard data for shipboard machinery and equipment
- BS ISO 19848:2024 Ships and marine technology. Standard data for shipboard machinery and equipment
- 24/30487130 DC BS EN 50566:2017/A2:2024 Product standard to demonstrate the compliance of wireless communication
- BS IEC 61360-7:2024 Standard data element types with associated classification scheme
- 24/30486472 DC - Product standard
- KS M ISO 4259-4 석유 및 관련 제품 — 측정 방법과 결과의 정밀도 — 제4부: 개별 실험실에서 표준 시험방법의 실행에 대한 ‘통계적 관리’ 상태를 확인하기 위한 통계적 관리도의 사용
- KS C IEC 61340-4-7 정전기학 — 제4-7부: 구체적 적용 분야에 대한 표준 시험방법 — 이온화
- KS C IEC 61340-4-8 정전기학 — 제4-8부: 구체적 적용 분야에 대한 표준 시험방법 — ESD 차폐성 — 봉투
- KS C IEC 61340-4-6 정전기학 — 제4-6부: 구체적 적용 분야에 대한 표준 시험방법 — 손목접지대
- 24/30485973 DC standard
- BS EN 14662-1:2023 - TC Tracked Changes. Ambient air quality. Standard method for measurement of benzene concentrations
- KS C IEC 61837-2 주파수 제어 및 선택을 위한 표면 실장형 압전 장치 — 표준 아웃라인 및 단자 리드 연결 — 제2부: 세라믹 함체
- 24/30485462 DC BS EN IEC 61753-1 Fibre optic interconnecting devices and passive components - Performance standard