【国外标准】 Standard Test Methods for Percent Solids in Titanium Dioxide Slurries
本网站 发布时间:
2024-02-28
开通会员免费在线看70000余条国内标准,赠送文本下载次数,单本最低仅合13.3元!还可享标准出版进度查询、定制跟踪推送、标准查新等超多特权!  
查看详情>>

适用范围:
4.1 These test methods are intended as a quick and reliable procedure for measuring the titanium dioxide pigment content of aqueous slurries. Included with the pigment content in the percent solids are the various nonvolatile additives used in preparing a stable slurry. Because the aluminum and silica oxide treatments on the more highly treated titanium dioxide pigments may change somewhat with prolonged drying, in the oven method the solids of the slurry are considered dry after heating at 105°C for 60 to 65 min. The high temperature associated with the infrared moisture analyzer may also effect a change in the aluminum and silica oxide treatment on highly treated TiO2 products. Therefore, care in selection of time and temperature are critical to obtain accurate results with the infrared method. With the short duration of test associated with the microwave drying system, overdrying is not a concern.1.1 These test methods cover the determination of the weight percent of solids in aqueous slurries of titanium dioxide pigments by either the use of a gravity-convection oven (Method A), infrared radiation moisture analyzer (Method B), or a microwave drying system (Method C).1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.1.3 This test standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
标准号:
ASTM D3926-05(2019)
标准名称:
Standard Test Methods for Percent Solids in Titanium Dioxide Slurries
英文名称:
Standard Test Methods for Percent Solids in Titanium Dioxide Slurries标准状态:
Active-
发布日期:
-
实施日期:
出版语种:
- 推荐标准
- ASC X9 IR 01-2019 Informative Report - Quantum Computing Risks to the Financial Services Industry
- ASC X9 TR 100-2019 Organization of Check-related Payments Standards Part 1: Organization of Standards Part 2: Definitions used in Standards
- ASC X9 TR 50-2019 Quantum Techniques in Cryptographic Message Syntax (CMS)
- ASTM 51026-23 Standard Practice for Using the Fricke Dosimetry System
- ASTM 52303-24 Standard Guide for Absorbed-Dose Mapping in Radiation Processing Facilities
- ASTM A1-00(2018) Standard Specification for Carbon Steel Tee Rails
- ASTM A1000/A1000M-17(2023) Standard Specification for Steel Wire, Carbon and Alloy Specialty Spring Quality
- ASTM A1001-18 Standard Specification for High-Strength Steel Castings in Heavy Sections
- ASTM A1002-16(2020) Standard Specification for Castings, Nickel-Aluminum Ordered Alloy
- ASTM A1004/A1004M-99(2018) Standard Practice for Establishing Conformance to the Minimum Expected Corrosion Characteristics of Metallic, Painted-Metallic, and Nonmetallic-Coated Steel Sheet Intended for Use as Cold Formed Framing Members
- ASTM A1009-18 Standard Specification for Soft Magnetic MnZn Ferrite Core Materials for Transformer and Inductor Applications
- ASTM A101-04(2019) Standard Specification for Ferrochromium
- ASTM A1010/A1010M-13(2018) Standard Specification for Higher-Strength Martensitic Stainless Steel Plate, Sheet, and Strip
- ASTM A1012-10(2021) Standard Specification for Seamless and Welded Ferritic, Austenitic and Duplex Alloy Steel Condenser and Heat Exchanger Tubes With Integral Fins
- ASTM A1015-01(2018) Standard Guide for Videoborescoping of Tubular Products for Sanitary Applications